Zinc Sulfide is an inorganic compound with the chemical formula ZnS. ZnS is a good infrared (IR) optical material. Zns can be transparent and used windows for visible optics or infrared optics. Stanford Electronics has rich experience in manufacturing and supplying high-quality Optical Products.
Related products: Zinc Sulfide (ZnS) Evaporation Materials, Zinc Sulfide (ZnS) Powder/Chunk/Lumps, Infrared Crystal Zinc Sulfide
Zinc Sulfide (ZnS) Wafer is made from high-purity ZnS, an insoluble material with excellent IR optical properties. It offers consistent refractive index and transmits well in the 8–12 μm range. Multispectral ZnS is also effective from 3–5 μm.
Compared to Zinc Selenide (ZnSe), ZnS is harder, stronger, and more cost-effective, making it ideal for demanding applications like missile cowlings and military aircraft IR windows.
|
Purity |
2N, 3N, 4N |
|
Crystal Structure |
Polycrystalline |
|
Melting Point |
1830℃ |
|
Density |
4.08g/cm3 |
|
Refractive Index |
2.3 at 10.6μm |
|
Growth Method |
Chemical Vapor Deposition |
|
Standard Size |
Φ10.0mm x 1.0mmΦ25.4mm x 3.0mm Or customized |
|
Roughness |
Ra: 5~10nm or <1.5nm |
|
Polishing |
Double size optical-polished/ Epi-polished |
|
Chamfer |
0.25mm*45° |
Used in infrared detectors, infrared windows, and optical coatings.
Used in infrared imaging sensors, ultraviolet detectors, and laser devices.
Used as a substrate in zinc sulfide-based scintillation detectors.
Our Zinc Sulfide (ZnS) Wafer is carefully handled during storage and transportation to preserve the quality of our product in its original condition.
|
Purity |
2N, 3N, 4N |
|
Crystal Structure |
Polycrystalline |
|
Melting Point |
1830℃ |
|
Density |
4.08g/cm3 |
|
Refractive Index |
2.3 at 10.6μm |
|
Growth Method |
Chemical Vapor Deposition |
|
Standard Size |
Φ10.0mm x 1.0mmΦ25.4mm x 3.0mm Or customized |
|
Roughness |
Ra: 5~10nm or <1.5nm |
|
Polishing |
Double size optical-polished/ Epi-polished |
|
Chamfer |
0.25mm*45° |